摘要
利用X射线衍射仪、扫描电镜和比表面仪研究了WO3还原成W粉过程中的相结构、粉末形貌和粒度的演变过程及机理。结果表明WO3在还原过程中依次转变为WO2.90、WO2.72、WO2,最终被还原成W。在WO3氢还原成W粉的过程中,WO3具有的平滑规则六面体形貌会转变为粗糙六面体,并随着还原过程进行,较大的二次颗粒分解成小颗粒。在WO3氢还原成WO2.90和WO2.72的过程中,粉末的比表面积不断增大,粉末粒度不断减小,但在WO2.72还原为WO2和WO2还原为W的过程中,粉末比表面减小,粉末的粒度不断增大。
The phase structure, morphology and particle size evolutions of tungsten oxide reduced by hydrogen were studied by X-ray diffractometer, scanning electron microscope and specific surface area meter. It is shown that the phase structure evolution is WO3 WO2.90- WO2. 72-WO2-W. The surface morphology of powder changes from a smooth to a rough particle and eventually the bigger secondary particles turn to several smaller particles. The specif- ic surface area of the powder increases during WO3 reducing to WO290-WO2.72, while specific surface area of the powder decrease when WO2.72 reducing to WO2 and WO2 reducing to W.
出处
《粉末冶金工业》
CAS
北大核心
2012年第4期26-29,共4页
Powder Metallurgy Industry
基金
国家自然科学基金(50801037
51071082)
教育部博士学科点专项基金(20103601110001)
教育部长江学者和创新团队发展计划(IRT0730)
教育部新世纪优秀人才支持计划(2010年度)
关键词
氢还原氧化钨
相结构
粉末形貌
粒度
hydrogen reduced tungsten oxide
phase structure
powder morphology
particle size