通过湿磨法,将钒-磷-氧(V-P-O)氧化物负载于钛硅干凝胶(TiO_2-SiO_2)上,制备了V-P-O/TiO_2-SiO_2氧化物催化剂,并运用BET,XRD,TEM及XPS等技术考察了润湿剂,V-P-O的含量及焙烧条件对催化剂结构的影响.由BET方法发现,以异丁醇为润湿剂对催化剂表面积影响较小.XRD和TEM考察结果表明,所制备的催化剂有较高的热稳定性.通过XPS分析,证实钒元素主要以V(Ⅳ)价态存在于催化剂的表面.V-P-O/TiO_2-SiO_2催化剂在丙烷氧化反应中显示了良好的催化性能.
Highly dispersed vanadium - phosphorus oxide (V - P - O)/titania - silica xerogel (TiO2 -were prepared by the method of wet mulling. The effects of the liquid medium, loading of V - P - O and the calcination temperature on the structure of catalysts were investigated by BET, XRD, TEM and XPS. BET shows that isobutanol as the liquid medium causes less change to the surface area of catalysts. XRD and TEM show that the prepared catalysts possess high thermal - stability up to 923K. XPS analysis shows that the vanadium on the surface can be stabilized mainly in the state of V( IV ) . The test oxidation of propane was also carried out with the resulting catalysts.
出处
《化学学报》
SCIE
CAS
CSCD
北大核心
2000年第2期214-217,共4页
Acta Chimica Sinica
基金
国家科委攀登预选项目
关键词
钛硅干凝胶
丙烷氧化
钒氧化物
催化剂
丙烯酸
vanadium - phosphorus - oxide catalysts
titania - silica xerogel
oxidation of propane