摘要
采用高温固相反应法制备了La2O2S∶Tb3+、La2O2S∶Tb3+,RE3+(RE=Dy,Gd,Ce,Sm)荧光粉样品并进行了相关表征。结果表明,合成样品的晶体结构与La2O2S相同,为六方晶系;荧光粉颗粒的形貌多为长方形片状;发射光谱由494 nm、545 nm、587 nm、622 nm的一系列锐发射峰组成。研究发现Tb3+的掺杂浓度对样品主发射峰545 nm的发光强度影响很大,且在摩尔分数x(Tb3+)=0.02时达到最强。稀土离子Dy3+、Gd3+对La2O2S∶Tb3+荧光粉的发光有明显的敏化作用。
La2O2S：Tb3＋,La2O2S：Tb3＋,RE3＋（RE=Dy,Gd,Ce,Sm） phosphors are synthesized by solid-state reaction method.XRD result shows that all the synthesized phosphors are La2O2S with a hexagonal crystal structure.The samples are characterized by SEM and Fluorescence spectrophotometer respectively.The particles of the synthesized phosphors are basically sheet restangle in shape.The emission spectrum is composed by a series of sharp peaks,located at 494 nm,545 nm,587 nm,622 nm respectively.The main emission peak is at 545 nm（5D4→7F5）,which results in a green-emitting.It is also found that the molar ratio of Tb3＋ plays a very important role in the emission spectrum.When the molar ratio of Tb3＋ is 0.2,the green-emitting becomes strongest.In the Dy3＋,Gd3＋ doped La2O2S：Tb3＋ crystals,the Dy3＋,Gd3＋ ions strongly sensitize the luminescence of the Tb3＋ ions.
出处
《稀土》
EI
CAS
CSCD
北大核心
2012年第1期11-14,共4页
Chinese Rare Earths
基金
湖南省教育厅项目资助(09C640)
长沙市科技局项目资助(K041058-12)
关键词
硫氧化镧
铽
固相反应法
光致发光
敏化
LI Qi-hua,LEI Chun-hua,WANG Ping,ZHANG Fan,ZHANG Jia-ying（College of Chemistry and Chemical Engineering,Hunan Normol University,Changsha 410081,China）