TSCR试制低碳低硅无取向电工钢织构的演变 被引量:1

Texture Evolution of Low-Carbon and Low-Silicon Non-Oriented Electrical Steel Produced by TSCR
原文传递
导出
摘要 研究了模拟TSCR流程生产的低碳低硅无取向电工钢在热轧-冷轧-退火过程中织构的演变。对热轧板采用EBSD技术进行织构的测定,而对冷轧板和退火板采用X射线衍射技术进行了织构的测定。结果表明:热轧板沿板厚方向织构变化比较明显,在1/10处主要织构为α纤维织构和γ纤维织构;在1/4厚度处出现了较强的γ纤维织构;在1/2厚度处主要为较强的{001}〈110〉织构,其他织构分布漫散。冷轧板表面和中心处主要织构均为α纤维织构和γ纤维织构,但是在中心处两织构强度都显著减弱。退火板表面和中心处α纤维织构基本消失,γ纤维织构织构进一步加强,出现了{110}〈001〉高斯织构和{001}〈010〉立方织构。 Texture evolution of low-carbon and low-silicon non oriented electrical steel produced by simulating TSCR in hot roiling, cold roiling and annealing process was investigated. The texture of hot rolled strip was measured by EBSD, yet the texture of cold rolled strip and annealed strip was measured by X-ray diffraction technology. The resuits show that the texture intensity along the thickness direction in the hot roiled strip change obviously, there are mostly a-fibre texture and 7-fibre texture in the 1/10 thickness. Quite strong 7 texture appears in the 1/4 thickness. There is mainly strong { 001 } (110)texture in the 1/2 thickness, and the other textrue distribute dispersedly. In the surface and center of the cold rolled strip, the main texture are a-fibre and γ fibre texture, but both of the texture are weaked obviously in the center. In the surface and center of the annealed strip, the a fibre texture disappears ba sically and the γ-fibre texture strengthen a lot. Meanwhile there are {110 } (001)goss texture and {001} (010)cubic texture.
出处 《钢铁》 CAS CSCD 北大核心 2012年第1期78-81,共4页 Iron and Steel
基金 国家自然科学基金 宝山钢铁股份有限公司联合资助项目(50934009)
关键词 TSCR 低碳 低硅 无取向电工钢 织构 TSCR low carbon low silicon non-oriented electrical steel texture
  • 相关文献

参考文献13

二级参考文献22

  • 1K.,ЛБ,张德春.热轧条件对电工钢轧件织构形成的影响[J].国外钢铁,1995,20(11):62-65. 被引量:2
  • 2张新明,李赛毅.金属材料织构的研究及其发展[J].中国科学基金,1995,9(3):26-30. 被引量:11
  • 3毛卫民 张新明.晶体材料织构定量分析[M].北京:冶金工业出版社,1995.. 被引量:24
  • 4毛卫民 赵新兵.金属的再结晶与晶粒长大[M].北京:冶金工业出版社,1998.32-34. 被引量:2
  • 5[3]Tomida T,Tanaka T.Development of (100) Texture in Silicon Steel Sheets Removal of Manganese and Decarburization[J].ISIJ Inter.1995,35(5):548-556. 被引量:1
  • 6[6]Sano N,Tomida T.Fine-Grained and Cube-Textured Si-Steel Sheet Coil By Oxide-Separator-Induced Decarburization[J].IEEE Transactions on Magnetics,2002,38(5):3198-9140. 被引量:1
  • 7[7]Boer B D,Wieting J.Fornation of a Near (100)[011]Recrystallization Texture in Electrical steels[J].Scripta Materialia,1997,37(6):753-760. 被引量:1
  • 8Kubota T,Fujikura M,Ushigami Y.Recent Progress and Future Trend on Grain-Oriented Silicon Steel[J].J Magn Magn Mmater,2000,215-216(2):39-73. 被引量:1
  • 9LIANG Z,XU J,WANG F.Determination of ODF of Polycrystalline Materials From Incomplete Pole Figures[A].Nagashima S eds.Proc 6th Int Conf on Textures of Materials[C].Tokyo:ISIJ,1981.1259-1265. 被引量:1
  • 10Meyer L.带钢轧制过程中材料性能的优化[M].赵辉译.北京:冶金工业出版社,1996. 被引量:3

共引文献168

同被引文献8

引证文献1

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部