摘要
The probability, main effect factors and diffusion theory of structural superplastic diffusion bonding of W6Mo5Cr4V2/45 steel have been observed and analyzed by means of tensile test at the room temperature, scanning electron microscope and microhardness test. Results show that after fine graining treatment and short time superplastic pressing formation under the conditions of superplastic temperature and strain rate, W6Mo5Cr4V2/45 specimens can achieve solid state diffusion bonding and the property of welded area is the same as the other parts in the specimen. The diffusion path of carbon element is intergranular and of dislocation.
The probability, main effect factors and diffusion theory of structural superplastic diffusion bonding of W6Mo5Cr4V2/45 steel have been observed and analyzed by means of tensile test at the room temperature, scanning electron microscope and microhardness test. Results show that after fine graining treatment and short time superplastic pressing formation under the conditions of superplastic temperature and strain rate, W6Mo5Cr4V2/45 specimens can achieve solid state diffusion bonding and the property of welded area is the same as the other parts in the specimen. The diffusion path of carbon element is intergranular and of dislocation.