摘要 The interfacial shear property of steel-mushy aluminum bonding plate was studied, and the relationship between aluminum solid fraction and the interfacial shear strength of bonding plate was determined. The results showed that when aluminum solid fraction is 34.3 %, the maximum interfacial shear strength of bonding plate is 71 .0 MPa. The interfacial shear property of steel-mushy aluminum bonding plate was studied, and the relationship between aluminum solid fraction and the interfacial shear strength of bonding plate was determined. The results showed that when aluminum solid fraction is 34.3 %, the maximum interfacial shear strength of bonding plate is 71 .0 MPa.

作者 Peng Zhang Yunhui Du Xueping Ren Yonglin Kang Hanwu Liu Jianzhong Cui Limin Ba(Material Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China)(Metal Forming Department, Northeastern University, Shenyang 110006

出处《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 1999年第3期193-195,共3页 矿物冶金与材料学报（英文版）

关键词 steel-mushy aluminum bonding plate solid fraction interfacial shear strength steel-mushy aluminum bonding plate solid fraction interfacial shear strength

分类号 TG142 [一般工业技术—材料科学与工程]

引文网络
相关文献

1Cao, Shunhua.FRACTURE STRENGTH OF WC-Co ALLOYS[J].中国有色金属学会会刊：英文版,1997,7(3):55-57.
2Bashchenko A.P.,Knokhin V.G.,Beliavsky P.B.,Traino A.I ..Improvement of mechanical properties of steel sheet[J].广东有色金属学报,2005,15(2):563-565.
3陈迎春,刘会杰,冯吉才.Friction stir welding of 2219-T6 aluminum alloy[J].中国有色金属学会会刊：英文版,2005,15(S2):75-78.
4ZHAO Xi-qing,PAN Tao,WANG Qing-feng,SU Hang,YANG Cai-fu,YANG Qing-xiang.Effect of Tempering Temperature on Microstructure and Mechanical Properties of Steel Containing Ni of 9%[J].Journal of Iron and Steel Research International,2011,18(5):47-51. 被引量：10
5王春生,殷世强,陈宇,信英华.Strength and microstructure of 2091 Al-Li alloy TIG welded joint[J].China Welding,2000,9(1):50-54.
6S.P. Lu,Y.Guo and L.S. Chen(Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110015, China).PREPARATION AND ITS WEAR RESISITANCE OF WC-Co/NiCrBSi METALLURGICAL BONDED COMPOSITE COATING[J].Acta Metallurgica Sinica(English Letters),2000,13(3):857-861.
7Wang Zhenliang,Ju Jikui,Zhang Yuzhen,Shen Hanliang and Zhang Zhongfa.Welding between Antirust Aluminum and Stainless Steel[J].IMP & HIRFL Annual Report,1996(1):166-167.
8Zhang, Erlin, Yang, Bo, Zeng, Songyan, Ma, Mingzhen.MICROSTRUCTURES AND MECHANICAL PROPERTIES OF SEMI-SOLID EXTRUDED IN-SITU Al-4.5Cu-0.8Mg/TiCp COMPOSITES[J].中国有色金属学会会刊：英文版,1998,8(2):117-121.
9P.Zhang,B.Z Guand B. Ling (Beijing Institute of Aeronautical Materials, Beijing 100095, China).STRESS CORROSION CRACKING IN 16NiCo STEEL[J].Acta Metallurgica Sinica(English Letters),1997,10(3):256-262.
10Deng,Zhiqian,Xie,Haitao(Department of Materials Seience and Engineering,Central South University of Technology,Changsha 410083).INFLUENCE OF HEAT TREATMENT PROCESSES ON MECHANICAL PROPERTIES OF ACu－Ni－AI－Ti ALLOY[J].中国有色金属学会会刊：英文版,1994,4(2):47-51.

International Journal of Minerals,Metallurgy and Materials

1999年第3期

浏览历史

内容加载中请稍等...

Influence of aluminum solid fraction on property of steel-mushy aluminum bonding plate

相关作者

相关机构

相关主题

浏览历史