The free energy change for the reduction-diffusion reaction which was used to prepare the DyFe_2 D_y2 O_3(s) + 3Ca(g) + 4Fe(s) = 3C_aO(s) + 2D_yFe_2(s) intermetallic compound powder was calculated. The reduction-diffusion experiments were carried out at 1073, 1123. 1273 and 1373 K respectively using powders of D_y2O_3, iron, and calcium grains as raw materials. XRD and EDX analysis confirmed that D_yFe_2 was formed by the diffusion of Dy into Fe.
The free energy change for the reduction-diffusion reaction which was used to prepare the DyFe_2 D_y2 O_3(s) + 3Ca(g) + 4Fe(s) = 3C_aO(s) + 2D_yFe_2(s) intermetallic compound powder was calculated. The reduction-diffusion experiments were carried out at 1073, 1123. 1273 and 1373 K respectively using powders of D_y2O_3, iron, and calcium grains as raw materials. XRD and EDX analysis confirmed that D_yFe_2 was formed by the diffusion of Dy into Fe.