Polyaniline-barium titanate (PAn-Ba-TiO3) ultrafine composite particles were prepared by the oxidative polymerization of aniline with H2O2 while barium titanate nanoparticles were synthesized with a sol-gel method. The infrared spectrogram shows that the polymerization of PAn in the hybrid process of PAn-BaTiO3 is similar with the polymeric process of pure aniline, and there is interaction of PAn and BaTiO3 in the PAn-Ba-TiO3. SEM and TEM results show that the average diameter of the composite particles is 1.50μm and the diameters of BaTiO3 nanoparticles are 5 - 15 nm in the composite particle. The electrical conductivity of the ultrafine com-posite particles is transformable from 10°to 10-11S/cm by equilibrium doping or dedoping method using various concentration of HCl or NaOH solutions.
Polyaniline-barium titanate (PAn-Ba-TiO3) ultrafine composite particles were prepared by the oxidative polymerization of aniline with H2O2 while barium titanate nanoparticles were synthesized with a sol-gel method. The infrared spectrogram shows that the polymerization of PAn in the hybrid process of PAn-BaTiO3 is similar with the polymeric process of pure aniline, and there is interaction of PAn and BaTiO3 in the PAn-Ba-TiO3. SEM and TEM results show that the average diameter of the composite particles is 1.50μm and the diameters of BaTiO3 nanoparticles are 5 - 15 nm in the composite particle. The electrical conductivity of the ultrafine com-posite particles is transformable from 10°to 10-11S/cm by equilibrium doping or dedoping method using various concentration of HCl or NaOH solutions.
基金
Funded by Chinese National Natural Science Foundation (No.29674021) and Key Foundation (No. 59832090). and Open Foundation from State Key Lab. of Advanced Technology for Materials Synthesis and Processing.