Ni Cr based alloys with a wide temperature range self lubrication were made by hot pressing the mixture powder of alloyed Ni Cr powder, elemental Mo, Al, Ti and B powders and MoS 2 powder. The mechanical and tribological properties of these alloys when rubbing with Al 2O 3 ceramics and W18Cr4V high speed steel were measured in the temperature range of 20～700 ℃, and the mechanisms of self lubrication and wear resistance were studied. The results showed that the alloy containing 10% MoS 2 has the best combination of mechanical properties, antifriction and wear resistance. Over a wide temperature range from 20 ℃ to 700 ℃, when rubbing with Al 2O 3, its friction coefficient and wear rate are 0.19～0.3 and (1.1～1.5)10 -14 m 3/(N·m), respectively; when rubbing with the high speed steel, those values are 0.18 ～ 0.26 and (0.6～3.2)×10 -15 m 3/(N·m), respectively.
Ni Cr based alloys with a wide temperature range self lubrication were made by hot pressing the mixture powder of alloyed Ni Cr powder, elemental Mo, Al, Ti and B powders and MoS 2 powder. The mechanical and tribological properties of these alloys when rubbing with Al 2O 3 ceramics and W18Cr4V high speed steel were measured in the temperature range of 20～700 ℃, and the mechanisms of self lubrication and wear resistance were studied. The results showed that the alloy containing 10% MoS 2 has the best combination of mechanical properties, antifriction and wear resistance. Over a wide temperature range from 20 ℃ to 700 ℃, when rubbing with Al 2O 3, its friction coefficient and wear rate are 0.19～0.3 and (1.1～1.5)10 -14 m 3/(N·m), respectively; when rubbing with the high speed steel, those values are 0.18 ～ 0.26 and (0.6～3.2)×10 -15 m 3/(N·m), respectively.
出处
《中国有色金属学会会刊：英文版》
CSCD
2000年第3期328-327,329-331,共5页
Transactions of Nonferrous Metals Society of China
基金
Project!5 95 710 62supportedbytheNationalNaturalScienceFoundationofChina