摘要
SrTiO 3 capacitor varistor multifunction ceramics is fabricated by a single sintering process. The research is carried out, mainly aimed at the influence of the doped Ag + on multifunction characteristics in SrTiO 3 ceramics and its mechanism. The results show that the density of grain boundary acceptor state increases effectively due to the fact that Sr 2+ on grain surface is substituted by doped Ag distributing at grain boundary in form of Ag + during the course of oxidizing annealing, which is proposed to be the fundamental reason for understanding the significant difference of both the dielectric properties and varistor properties in SrTiO 3 ceramics samples with various Ag + contents.
SrTiO 3 capacitor varistor multifunction ceramics is fabricated by a single sintering process. The research is carried out, mainly aimed at the influence of the doped Ag + on multifunction characteristics in SrTiO 3 ceramics and its mechanism. The results show that the density of grain boundary acceptor state increases effectively due to the fact that Sr 2+ on grain surface is substituted by doped Ag distributing at grain boundary in form of Ag + during the course of oxidizing annealing, which is proposed to be the fundamental reason for understanding the significant difference of both the dielectric properties and varistor properties in SrTiO 3 ceramics samples with various Ag + contents.
出处
《中国有色金属学会会刊：英文版》
CSCD
2000年第1期69-72,共4页
Transactions of Nonferrous Metals Society of China