摘要
The reduction behavior of iron ore pellets containing carbon under non-isothermal condition in the temperature range from 573 to 1373 K was investigated in a laboratory scale setup. The test results show that carbon content has no obvious effect on reduction degree of composite pellets (C/O mole ratio=1.0) by CO in the temperature range from 573 to 1373 K under linear temperature-rising program; reduction degree of iron ore pellets containing carbon is large in 90%CO-10%CO2 mixture than that of in 100%CO atmosphere or in 80%CO-20%CO2 mixture; the s type temperature-rising program has a better effect than that of linear one in increasing the reduction degree; and reduction degree of slower linear temperature-rising program is greater than that of faster one, but the final reduction degrees, i.e., those at the highest temperature are about the same for various CO partial pressures or temperature-rising programs. The kinetic analysis also shows that the reduction of iron ore-carbon composite pellets by CO or CO-CO2 mixture under non-isothermal condition should be controlled by surface reaction, and the apparent reduction activation energy changes with the reduction progress under various test conditions.
The reduction behavior of iron ore pellets containing carbon under non-isothermal condition in the temperature range from 573 to 1373 K was investigated in a laboratory scale setup. The test results show that carbon content has no obvious effect on reduction degree of composite pellets (C/O mole ratio=1.0) by CO in the temperature range from 573 to 1373 K under linear temperature-rising program; reduction degree of iron ore pellets containing carbon is large in 90%CO-10%CO2 mixture than that of in 100%CO atmosphere or in 80%CO-20%CO2 mixture; the s type temperature-rising program has a better effect than that of linear one in increasing the reduction degree; and reduction degree of slower linear temperature-rising program is greater than that of faster one, but the final reduction degrees, i.e., those at the highest temperature are about the same for various CO partial pressures or temperature-rising programs. The kinetic analysis also shows that the reduction of iron ore-carbon composite pellets by CO or CO-CO2 mixture under non-isothermal condition should be controlled by surface reaction, and the apparent reduction activation energy changes with the reduction progress under various test conditions.