摘要
The rare-earth hard magnets with lower temperature coefficient, including Nd_2Fe_ 14B/Fe_3B-ferrite compound bonded magnets and Sm_ 0.8RE_ 0.2 (Co_ balFe_ 0.22Cu_ 0.06Zr_ 0.03)_ 7.4(RE=Gd, Er) sintered magnets, were studied. The result shows that the addition, that dope ferrite magnetic powder to double-phase nanocomposite Nd_2Fe_ 14B/Fe_3B magnetic powder, can make β_ jH_c to be obviously decreased. Similarly, the effect of homogeneous heating treatment on magnetic properties was studied. Doping heavy rare earth elements to the 2∶17-type SmCo magnet material powders shows that the sintered magnets obtained lower temperature coefficient, and enhanced magnets temperature stability.
The rare-earth hard magnets with lower temperature coefficient, including Nd_2Fe_ 14B/Fe_3B-ferrite compound bonded magnets and Sm_ 0.8RE_ 0.2 (Co_ balFe_ 0.22Cu_ 0.06Zr_ 0.03)_ 7.4(RE=Gd, Er) sintered magnets, were studied. The result shows that the addition, that dope ferrite magnetic powder to double-phase nanocomposite Nd_2Fe_ 14B/Fe_3B magnetic powder, can make β_ jH_c to be obviously decreased. Similarly, the effect of homogeneous heating treatment on magnetic properties was studied. Doping heavy rare earth elements to the 2∶17-type SmCo magnet material powders shows that the sintered magnets obtained lower temperature coefficient, and enhanced magnets temperature stability.