摘要
In order to encapsulate and controlled-release bioactive proteins,three fibrous membranes,i.e.,poly（L-lactide-co-glycolide）（PLGA）,hybrid PLGA and chitosan（H-PLGA/CS）,and core/shell PLGA/CS （C-PLGA/CS）,were produced by emulsion electrospinning,co-electrospinning and coaxial electrospinning,respectively.Bovine serum albumin（BSA） was selected as a model protein.The loading efficiency of BSA in the PLGA membrane was 1.56%,lower than those of H-PLGA/CS（5.98%） and C-PLGA/CS（4.80%）.BSA release profiles from the three membranes showed initial burst releases in the first 7 d and then sustained release for 28 d.Cumulative releases at the end of the releasing period,28 d,from the above three membranes were nearly 63%,88% and 94%,respectively,indicating that the introduction of chitosan and the core/shell fiber structure could enhance BSA release rate.In addition,all these electrospun membranes could retain their fibrous morphologies after in vitro release of BSA for 28 d.
In order to encapsulate and controlled-release bioactive proteins,three fibrous membranes,i.e.,poly（L-lactide-co-glycolide）（PLGA）,hybrid PLGA and chitosan（H-PLGA/CS）,and core/shell PLGA/CS （C-PLGA/CS）,were produced by emulsion electrospinning,co-electrospinning and coaxial electrospinning,respectively.Bovine serum albumin（BSA） was selected as a model protein.The loading efficiency of BSA in the PLGA membrane was 1.56%,lower than those of H-PLGA/CS（5.98%） and C-PLGA/CS（4.80%）.BSA release profiles from the three membranes showed initial burst releases in the first 7 d and then sustained release for 28 d.Cumulative releases at the end of the releasing period,28 d,from the above three membranes were nearly 63%,88% and 94%,respectively,indicating that the introduction of chitosan and the core/shell fiber structure could enhance BSA release rate.In addition,all these electrospun membranes could retain their fibrous morphologies after in vitro release of BSA for 28 d.
基金
Supported by the National Natural Science Foundation of China(Nos.50273027,50573055,30828008)
the Natural Science Foundation of Tianjin City,China(No.09JCZDJC18600)