背板失效与PET结晶度的关系 被引量:3

Relationship between failure of backsheets and crystallinity of pet
下载PDF
导出
摘要 本文研究了不同厂家背板湿热老化前后的力学性能、PET层结晶度以及红外吸收峰的变化,得出了背板失效与其PET层结晶度的关系。 In this paper, mechanical properties, crystallinity of PET layer and infrared absorption peak of backsheets from different factories are studied following the changes before and after hydrothermal aging, and relationship between failure of backsheets and crystallinity of PET layer is concluded.
出处 《中国建设动态(阳光能源)》 2011年第4期62-63,共2页
关键词 背板 湿热老化 失效 PET 结晶度 Backsheets Hydrothermal aging Failure PET Crystallinity
  • 相关文献

参考文献1

  • 1何曼君等编..高分子物理 修订版[M].上海:复旦大学出版社,1990:462.

同被引文献29

  • 1卢群英,等.聚酯组合物及其生产方法[P].CN:101955579,2011-01-26. 被引量:2
  • 2卢群英,祁华,望月克彦.一种共聚酯及其生产方法[P].中国专利:102898632A,2013-01-30. 被引量:1
  • 3李旭,本田圭介.具有优异耐水解性能的阻燃性聚酯及其制备方法[P].中国专利:101186688A,2008-05-28. 被引量:1
  • 4高信敬,陈丽华,吴志郎,等.一种耐水解聚酯组合物及其制备方法[P].中国专利:1312327,2001-09-12. 被引量:1
  • 5OSTERWALD C R, ANDERBERG A, RUMMEL S, et al. Degradation analysis of weathered crystalline-silicon PV modules [ J ]. IEEE Photovohaic Specialists Conference, 2002 (5) : 1392 - 1395. 被引量:1
  • 6KIM N, KANG H, et al. Study on the degradation of different types of backsheets used in PV module under accelerated conditions [ J ]. Solar Energy Materials & Solar Cells, 2014, 120:543 -548. 被引量:1
  • 7K1M N, PARK N, et al. Developing accelerated life test for backsheet used in PV module and correlation study between field and accelerated conditions [ J ]. Photovohaic Specialists Conference, 2011(7) : 62 -165. 被引量:1
  • 8OSTERWALD C R, MCMAHON T J. History of accelerated and qualication testing of terrestrial photovohaic modules: a literature review [ J ]. Prog Photovolt : Res Appl, 2009,17 : 11 - 13. 被引量:1
  • 9RAHIMPOUR A, MADAENI S S, et al. Preparation and characterization of modified nano-porous PVDF membrane with high antifouling property using U V photo-grafting [ J ]. Applied Surface Science ,2009, 255:7455 - 7461. 被引量:1
  • 10LIU F, J1ANG L, YANG S Y. Ultra-violet degradation behavior of polymeric backsheets for photovoltaic modules [ J ]. Solar Energy, 2014,108:88 - 100. 被引量:1

引证文献3

二级引证文献7

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部