仲钼酸铵热分解过程的研究 被引量:5

RESEARCH ON THE PROCESS OF THE PYROLYTIC DECOMPOSITION OF AMMONIUM PARAMOLYBDATE
下载PDF
导出
摘要 通过TG-DSC分析仪和激光粒度分析仪对仲钼酸铵在空气中热分解过程进行分析,研究结果表明,仲钼酸铵在空气中的热分解过程经历了3个阶段:室温至222.6℃之间仲钼酸铵失去结晶水;222.6~240.7℃之间仲钼酸铵热分解了部分氨根离子;240.7~248.7℃之间氨根离子完全分解,同时有亚稳态的氧化钼生成,从248.7~322.5℃之间亚稳态的氧化钼发生相变生成了稳态的三氧化钼。与此同时,在322.5~500.0℃之间,温度对产物粒径的影响最大;在248.7~322.5℃之间,温度对产物粒径的影响次之;在室温至322.5℃之间,温度对产物粒径的影响不明显。 The pyrolytic decomposition of ammonium paramolybdate was analyzed by TG-DSC and laser granulometer.The results show that there are three stages in the process of pyrolytic decomposition of ammonium paramolybdates in the air.The crystal water in ammonium paramolybdates got lost from room temperature to 222.6 ℃.The partial ammonia ion in ammonium paramolybdates was decomposed from 222.6 ℃ to 248.7 ℃,and metastable molybdenum oxide was formed.Metastable molybdenum oxide turned into molybdic oxide from 248.7 ℃ to 322.5 ℃.At the same time,the influence of temperature on the particle size of the decomposition was the greatest from 322.5 ℃ to 500.0 ℃,greater from 248.7 ℃ to 322.5 ℃ and not obvious from room temperature to 322.5 ℃.
机构地区 宿迁学院三系
出处 《中国钼业》 2011年第3期30-32,35,共4页 China Molybdenum Industry
关键词 仲钼酸铵 热分解 TG-DSC 粒径分布 ammonium paramolybdates pyrolytic decomposition TG-DSC particle size distribution
  • 相关文献

参考文献6

  • 1彭志辉..稀有金属材料加工工艺学[M],2003.
  • 2吴贤,张健,康新婷,荆鹏.钼粉的制备技术及研发现状[J].稀有金属材料与工程,2007,36(A03):562-566. 被引量:25
  • 3朱爱辉,王快社,张兵.钼在冶金工业中的应用[J].中国钼业,2006,30(5):8-12. 被引量:19
  • 4Kim D S, Kumsu Y, Wachs I E, et al. Physicochemical properties of MoO3 -'riO2 prepared by an equilibrium ad- sorption method[J]. J. Catal., 1989, 120(2): 325- 336. 被引量:1
  • 5Datta A K, Ha J W, Regalbuto J R. The controlled dis- persion of silica supported MOO3: The role of ammonia [J]. J. Catal., 1992, 133(1): 55-82. 被引量:1
  • 6Li C, Zhang H, Wang K L, et al. FT - IR emmission spectroscopic studies of the thermal decomposition of am- monium molybdate, Vanadate and Tungstate [ J]. Appl. Spectrosc. , 1993, 47 (1): 56-61. 被引量:1

二级参考文献39

共引文献41

同被引文献50

引证文献5

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部