通过在向列相液晶TEB30A中掺杂激光染料DCM和手性剂CB15制作了平面排列态液晶器件。采用Nd∶YAG倍频532 nm波段激光作为泵浦光源,测量分析了平行于液晶器件表面方向的受激辐射光谱。当泵浦光较弱时,观察到了染料DCM较宽的荧光辐射谱;随着泵浦光的逐渐增强,辐射谱带逐渐变窄,辐射峰中心波长约为610 nm,最小半峰全宽(FWHM)为11 nm。观察了在器件玻璃基板上施加交流电场后激光辐射的变化情况,结果显示,当外加电压<9 V时,辐射强度随着电压的增大逐渐减弱;当外加电压>9 V,辐射强度迅速衰减,谱线变宽,显示了较好的电场控制特性。文章认为这种现象主要是由于电场作用下液晶分子取向发生变化所致。
A planar texture device was prepared by doping a laser dye（DCM） and a chiral compound（CB15） into a nematic liquid crystal TEB30A.By using a second harmonic Q-switched Nd∶YAG pulsed laser（λ=532 nm） as pumping source,the emission spectrum of the device surface in the horizontal direction was measured and analyzed.It shows that a wide emission spectrum can be observed when the pump light is weak.With the increase of pump light,the stimulated emission spectrum is narrowed,and its center wavelength with a least Full Width of Half Maximum（FWHM）about 11 nm is at 610 nm.Moreover,by applying a AC voltage along the perpendicular direction to the surface of the device,the laser emission was also observed.When the applying voltage is less than 9 V,the lasing intensity is weakened with the increase of the voltage.When the applying voltage is greater than 9 V,the emission intensity is decreased sharply.These results can be attributed to the liquid crystal alignment changed on the applying electric field.
出处
《光学精密工程》
EI
CAS
CSCD
北大核心
2011年第7期1510-1514,共5页
Optics and Precision Engineering
基金
国家自然基金资助项目(No.60777011)
辽宁省自然科学基金资助项目(No.20102191)
辽宁省教育厅科技项目(No.L2010465)
关键词
激光辐射
染料掺杂
扭曲向列相液晶
电场控制
laser emission
dye doping
cholesteric liquid crystal
electric filed control