摘要
本文评述了定向凝固共晶多相复合陶瓷的制备方法， 并介绍了定向凝固 Ａｌ２ Ｏ３ Ｙ Ａ Ｇ 共晶复合材料优异的高温强度、热稳定性以及抗蠕变性断裂强度达３５０ ～４００ Ｍ Ｐａ ， 且从室温到２０７３ Ｋ 基本不变； 在１９２３ Ｋ 以上拉伸试验， 显示出由位错运动引发的塑性形变； 且观察到类似于金属的屈服现象这种复合材料经１９７３ Ｋ１０００ｈ 空气中热处理后的显微结构也十分稳定有望成为２１
This paper reviews the manufacturing method of the unidirectionally solidified eutectic composite A unidirectionally solidified Al 2O 3/YAG eutectic composite has superior flexural strength, thermal stability and creep resistance at high temperature up to 2073K For example, the flexural strength is 350～400MPa indepedent of testing temperature from room temperature to 2073K (just below its melting point of 2100K) During tensile test above 1923K, the eutectic composite shows the evidence of plastic deformation occurring by dislocation motion, and a yield phenomenon similar to many metals observed The microstructure of the composite is extremely stable after heat treatment at 1973K for 1000h in air atmosphere It may be expected that it would be a new heat resistant structural material in the twenty one century
出处
《无机材料学报》
SCIE
EI
CAS
CSCD
北大核心
1999年第4期513-519,共7页
Journal of Inorganic Materials
关键词
定向凝固
共晶
复合陶瓷
多相复合
unidirectional solidification, eutectic, alumina, garnet, composite