以MnSO4和(NH4)2S2O8为主要原料,Fe(NO3)3为添加剂,采用水热法制备了菜花状MnO2。运用XRD,SEM对制备的MnO2进行了形貌和结构分析。通过循环伏安、恒流充放电测试和交流阻抗研究了MnO2的电化学性能。结果表明,实验制备的MnO2为α型菜花状结构,其在6 mol/L的KOH电解液中及0～0.4 V的电位范围内表现出良好的超级电容性能,电流密度为100 mA/g时,其比容量达到176 F/g。
Cauliflower MnO2 was prepared by hydrothermal synthesis method by reacting MnSO4 and（NH4）2S2O8 with Fe（NO3）3.The samples were analyzed by X-ray diffraction（XRD） and scanning electron microscopy（SEM）.Cyclic voltammetry and galvanostatic charge-discharge were used to characterize the electrochemical performance of the samples.The results show that the prepared samples are α-MnO2.The particles are in a cauliflower shape.In an electrolyte of 6 mol/L KOH,electrode based on the MnO2 show perfect supercapacitor characterization in the potential region of 0～0.4 V.At a current density of 100 mA/g,a specific capacitance of 176 F/g is achieved.
出处
《河北科技大学学报》
CAS
北大核心
2011年第2期169-172,共4页
Journal of Hebei University of Science and Technology
基金
河北科技大学科研基金资助项目(XL200872
XL200908)
关键词
水热法
MNO2
超级电容器
比容量
hydrothermal synthesis
MnO2
supercapacitors
specific capacitance