A flower-like Eu^2＋ and Dy^3＋ co-doped SrAl2O4 long-lasting phosphorescent （LLP） phosphor was synthesized via the inorganic- salt-based sol-gel method. The crystal structure, morphology and optical properties of the composite were characterized. X-ray diffraction diffusion （XRD） data and DSC-TG curves of the phosphor revealed that the SrAl2O4 crystallites have been formed after the precursor was calcined at 900 ℃ and to be single-phase SrA1204 at 1100 ℃. The SEM photographs indicated that the sample exhibited a universal flower-like morphology with crystallite size of about l-2μm. After being irradiated with ultraviolet （UV） light, the flower-like phosphor emitted long-lasting green phosphorescence with an excitation peak at 365 nm and emission peak at 500 nm which was ascribed to the characteristic 5d-4f transition of Eu^2＋. Both the PL spectra and the luminance decay curve revealed that this phosphor exhibited efficient luminescence and long lasting properties.
A flower-like Eu^2＋ and Dy^3＋ co-doped SrAl2O4 long-lasting phosphorescent （LLP） phosphor was synthesized via the inorganic- salt-based sol-gel method. The crystal structure, morphology and optical properties of the composite were characterized. X-ray diffraction diffusion （XRD） data and DSC-TG curves of the phosphor revealed that the SrAl2O4 crystallites have been formed after the precursor was calcined at 900 ℃ and to be single-phase SrA1204 at 1100 ℃. The SEM photographs indicated that the sample exhibited a universal flower-like morphology with crystallite size of about l-2μm. After being irradiated with ultraviolet （UV） light, the flower-like phosphor emitted long-lasting green phosphorescence with an excitation peak at 365 nm and emission peak at 500 nm which was ascribed to the characteristic 5d-4f transition of Eu^2＋. Both the PL spectra and the luminance decay curve revealed that this phosphor exhibited efficient luminescence and long lasting properties.
基金
Project supported by the National Natural Science Foundation of China (20671042,50872045)
Natural Science Foundation of Guangdong Province (05200555,7005918)