摘要
采用共沉淀-喷雾干燥法制备YAG∶Ce3+荧光粉。前驱体经热处理、研磨、酸洗碱洗后形成荧光粉。研究了前驱体料浆浓度、热处理条件、研磨、酸洗碱洗对粉末晶相、颗粒形貌、粒度和发光性能的影响。研究发现:料浆浓度为0.2,0.4,0.6 mol/L时,前驱体颗粒形貌分别呈碎屑、光滑和褶皱状球形;无团聚光滑球形前驱体经1 100℃热处理4 h后,XRD未检测到杂相;继续升温至1 550℃,荧光粉相对亮度随之提高;酸洗碱洗能够去除碎屑,获无团聚荧光粉,提高相对亮度。
Co-precipitation together with spray dry processing was introduced to prepare YAG∶Ce^3＋ precursor first time.YAG∶Ce3＋ phosphor could be obtained after heat-treating,milling and further acid and alkali washing.Effects of spray suspension concentration,heat treatment temperature and the acid and alkali washing on particle morphology,type of crystal phase and photoluminescence（PL） intensity of the powder were investigated.The precursor particles appeared nearly spherical balls with fragments in the surface,smooth or rugged ones when the concentration of spray suspension was 0.2,0.4 and 0.6 mol/L,respectively.YAG phase could be obtained by heat-treating the smooth spherical precursor at 1 100 ℃ for 4 h.The PL intensity of the powder raised with heat-treating temperature increased up to 1 550 ℃.Agglomerate-free YAG∶Ce^3＋ phosphor with good preferences could be obtained by acid and alkali washing which could remove scraps adhering on particles and break aggregates between them.
出处
《发光学报》
EI
CAS
CSCD
北大核心
2010年第6期806-811,共6页
Chinese Journal of Luminescence
基金
福建省科技重大专项(2005HZ02-2)资助项目
关键词
共沉淀
喷雾
酸洗碱洗
白光LED
钇铝石榴石
co-precipitation
spray
acid and alkali wash
white LED
yttrium aluminum garnet