摘要
目的观察不同沉积时间下应用等离子镀膜法镀制渗氮类金刚石碳膜(N-DLC)的颜色改变规律,以期对临床应用有所指导。方法采用等离子镀膜机在纯钛表面先沉积TiN过渡层,再沉积N-DLC碳膜,通过目测及分光光度测色法对不同沉积时间下(10～80 min,间隔5 min)N-DLC碳膜的颜色进行测定,通过CIE1976 L*a*b*及Mussell表色系统定量评价其色度属性,并结合扫描电镜观察各个沉积时段N-DLC碳膜的表面形貌。结果纯钛表面N-DLC薄膜的颜色与沉积时间有较大关系,沉积时间为30 min时得到较亮的金黄色外观;扫描电镜观察随着沉积时间增加N-DLC碳膜表面逐渐晶化,晶相结构由稳定趋于杂化。结论当镀膜沉积时间为30 min时,可在纯钛表面得到金黄色外观的N-DLC碳膜,此时的晶相结构最稳定。
Objective The aim of this study was to observed the influence of deposition time on chromatics during nitrogen-doped diamond like carbon coating（N-DLC） on pure titanium by multi impulse arc plasma plating machine.Methods Applying multi impulse arc plasma plating machine to produce TiN coatings on pure titanium in nitrogen atmosphere,then filming with nitrogen-doped DLC on TiN in methane（10-80 min in every 5 min）.The colors of N-DLC were evaluated in the CIE1976 L＊a＊b＊ uniform color scale and Mussell notation.The surface morphology of every specimen was analyzed using scanning electron microscope（SEM） and X-ray photoelectron spectroscopy（XPS）.Results When changing the time of N-DLC coating deposition,N-DLC surface showed different color.Golden yellow was presented when deposition time was 30 min.SEM showed that crystallization was found in N-DLC coatings,the structure changed from stable to clutter by varying the deposition time.Conclusion The chromatics of N-DLC coatings on pure titanium could get golden yellow when deposition time was 30 min,then the crystallized structure was stable.
出处
《华西口腔医学杂志》
CAS
CSCD
北大核心
2010年第5期543-546,共4页
West China Journal of Stomatology
基金
福建省自然科学基金青年创新基金资助项目(2009D013)
西安工业大学光电工程学院国家薄膜重点实验室开放课题基金资助项目(ZSKJ-200709)
关键词
纯钛
表面改性
类金刚石
色度
结晶
pure titanium
surface modification
diamond like carbon
chroma
crystallization