超高强度冷轧双相钢组织与性能 被引量:21

Microstructure and properties of ultra-high strength cold-rolled dual phase steel
原文传递
导出
摘要 在Gleeble-3500热模拟试验机上进行冷轧超高强度双相钢的连续退火工艺研究,利用光学显微镜、扫描电镜、透射电镜和拉伸试验研究了连续退火过程中各个参数对1000MPa级冷轧双相钢组织性能的影响.结果表明:试验用钢在退火温度800℃下保温80s,可以得到抗拉强度为1030MPa、延伸率为14%超高强双相钢;随着退火温度的升高,屈服强度和抗拉强度降低.当退火温度为830℃时,显微组织中粒状的非马氏体组织明显增多.过时效温度低于300℃时,屈服强度和抗拉强度变化不大;当过时效温度超过300℃时,抗拉强度急剧下降,屈服强度先降低后升高,在过时效温度为360℃时开始出现屈服平台. The continuous annealing process of ultra-high strength cold-rolled dual phase steels was simulated using a Gleeble- 3500 thermal simulator. The effects of continuous annealing parameters on the microstructure and mechanical properties of the 1 000 MPa grade dual phase steel were investigated by optical microscope, scanning electron microscope, transmission electron microscope and tensile tests. It is shown that a dual phase (DP) steel with a tensile strength of 1 030 MPa and a total elongation of 14% was obtained after being soaked at 800 qC for 60 s. With the increase of annealing temperature, the yield strength and tensile strength decrease. When the annealing temperature reaches 830 ℃ , the volume fraction of granular non-martensite in the microstructure increases obviously. When the over-aging temperature is lower than 300 ℃ , the yield strength and the tensile strength change slightly. When the over-aging tempe'rature is higher than 300 ℃ , the tensile strength decreases strongly, whereas the yield strength reduces first and then increases. There is yield point elongation when the over-aging temperature is 360 ℃.
出处 《北京科技大学学报》 EI CAS CSCD 北大核心 2010年第10期1287-1291,共5页 Journal of University of Science and Technology Beijing
基金 国家自然科学基金资助项目(No.50904006) "十一五"国家科技支撑计划资助项目(No.2006BAE03A06)
关键词 双相钢 连续退火 显微组织 力学性能 dual phase steel continuous annealing microstructure mechanical properties
  • 相关文献

参考文献5

二级参考文献22

  • 1苏钰,符仁钰,李麟.马氏体含量对St12Q1和St37-2G双相钢力学性能的影响[J].上海金属,2004,26(4):8-12. 被引量:9
  • 2张丙,冯锋,万晓景.低碳低合金双相钢低温时效机理探讨[J].金属热处理学报,1994,15(2):7-12. 被引量:4
  • 3温东辉.金相组织对双相钢强度影响的研究[J].上海金属,2005,27(6):51-55. 被引量:22
  • 4Kot R A, Bramfitt B L. Fundamentals of Dual-phase Steels[M]. The Metallurgical Society of AIME, Warrendale, Pa. 1981. 被引量:1
  • 5Takasaki J, Irie T, Haga T, et al. Production of 35-45kgf/mm^2 cold rolled high strength steels with excellent press formibility by continuous annealing[J].Tetsu-To-Hagane, 1982(9) : 150 ~ 156. 被引量:1
  • 6Tobiyama Y, Osawa K, Hirata M. Development of 590MPa grade galvannealed sheet steels with dual phase structure[J]. Kawasaki Steel Technical Report,2000(42) : 19 ~ 23. 被引量:1
  • 7Rashid M S.Relationship Between Steel Microstructure and Formability[A].Davenport A T eds.Formable HSLA and Dual-Phase Steels[C].New York:TMS/AIME,1979.1. 被引量:1
  • 8Nakaoka K,Araki K,Kurihara K.Strength,Ductility and Aging Properties of Continuously-Annealed Dual-Phase HighStrength Sheet Steels[A].Davenport A T eds.Formable HSLA and Dual-Phase Steels[C].New York:TMS/AIME,1979.126. 被引量:1
  • 9Bhattacharya D. Developments in advanced high strength steels// The Joint International Conference of HSLA Steels 2005 and ISUGS 2005 Proceedings. Sanya, 2005:70 被引量:1
  • 10Rocha R O, Melo T M F, Pereloma E V, et al. Microstructural evolution at the initial stages of continuous annealing of cold rolled dual-phase steel. Mater Sci Eng A, 2005, 391 : 296 被引量:1

共引文献55

同被引文献140

引证文献21

二级引证文献107

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部