Grain growth kinetics of austenite in a hypoeutectoid steel（containing carbon of 0.35%）at 920 ℃ and in a hypereutectoid steel（containing carbon of 1%）at 980 ℃ for holding time ranging from 1 h to 6 h was investigated.The hypoeutectoid steel exhibited normal grain growth without solute drag hindrance with a time exponent（0.51）close to the theoretical value（0.5）.However,the grain growth of austenite in the hypereutectoid steel held up to 3 h was extremely slow,characterizing by a low value of time exponent（0.08）.Thereafter,a breakaway occurred and the grain growth in the hypereutectoid steel held from 3 h to 6 h progressed normally with a time exponent（0.52）close to the theoretical value（0.5）.
Grain growth kinetics of austenite in a hypoeutectoid steel（containing carbon of 0.35%）at 920 ℃ and in a hypereutectoid steel（containing carbon of 1%）at 980 ℃ for holding time ranging from 1 h to 6 h was investigated.The hypoeutectoid steel exhibited normal grain growth without solute drag hindrance with a time exponent（0.51）close to the theoretical value（0.5）.However,the grain growth of austenite in the hypereutectoid steel held up to 3 h was extremely slow,characterizing by a low value of time exponent（0.08）.Thereafter,a breakaway occurred and the grain growth in the hypereutectoid steel held from 3 h to 6 h progressed normally with a time exponent（0.52）close to the theoretical value（0.5）.