The Yb3＋-doped LiGd（MoO4）2 crystal with the size up to Φ20×30 mm3 has been grown by Czochralski technique.The polarized room temperature absorption and emission spectra have been investigated.This crystal exhibits a broad absorption band centered at 975 nm with an FWHM of 43 and 59 nm for π-and σ-polarization,respectively,and the corresponding maximal absorption cross-sections are 3.36 and 2.42×10-20 cm2.The emission broadband has an FWHM of 47 and 54 nm for π-and σ-polarization,respectively,with the corresponding emission cross sections of 3.92 and 3.34 × 10-20 cm2 at 1020 nm.The measured fluorescence lifetime is 287 μs.
The Yb3＋-doped LiGd（MoO4）2 crystal with the size up to Φ20×30 mm3 has been grown by Czochralski technique.The polarized room temperature absorption and emission spectra have been investigated.This crystal exhibits a broad absorption band centered at 975 nm with an FWHM of 43 and 59 nm for π-and σ-polarization,respectively,and the corresponding maximal absorption cross-sections are 3.36 and 2.42×10-20 cm2.The emission broadband has an FWHM of 47 and 54 nm for π-and σ-polarization,respectively,with the corresponding emission cross sections of 3.92 and 3.34 × 10-20 cm2 at 1020 nm.The measured fluorescence lifetime is 287 μs.
基金
supported by the National Natural Science Foundation of China (No. 60808033)
Natural Science Foundation of Jiangxi Province (No. 2008GZW0012)
the Science Project of the Education Commission of Jiangxi Province (No. GJJ08345)