对4根未腐蚀和16根腐蚀钢筋混凝土梁进行抗弯试验,研究重复荷载下高腐蚀率对钢筋混凝土梁变形、裂缝、承载力及破坏机理的影响。提出重复荷载下受腐蚀钢筋混凝土梁承载力计算公式。同时拟合出钢筋腐蚀率对钢筋混凝土受弯开裂的影响,并提出受腐蚀梁在重复荷载下的开裂荷载计算公式。
Deformation,cracking,bearing capacity and the failure mechanism of beams with corroded reinforcement under repeated loading were investigated.Twenty sample beams,including 4 uncorroded and 16 corroded reinforced concrete beams were tested under repeated loading.The effect of corrosion rate on the bearing capacity and flexural cracking was presented.Formulas for the bearing capacity and cracking load of corroded beams under repeated load were suggested.