Alpha-lipoic acid-loaded lipid nanoparticles(ALA-LNs) were prepared by high pressure homogenization method.The influences of storage conditions such as time and temperature on the physical and chemical storage stability of ALA-LNs were studied in details.The stability was evaluated by particle size and polydispersity index,morphology of ALA-LNs,and capacity of ALA loading.The dilution and pH stability of ALA-LNs suspensions were also studied.After three months storage,the mean size of ALA-LNs at 4 and 40 ℃ was increased by 2.68% and 3.62% compared with the original size,respectively.ALA-LNs stored at 40 ℃ had ellipsoid shape and the mean size was about 152 nm(SD=23.6).The loading capacity of ALA at 40 ℃ was much higher than those stored at other two temperatures.The good dilution and pH stability were also demonstrated.The sample had good fluidity even at 4 ℃.
Alpha-lipoic acid-loaded lipid nanoparticles（ALA-LNs） were prepared by high pressure homogenization method.The influences of storage conditions such as time and temperature on the physical and chemical storage stability of ALA-LNs were studied in details.The stability was evaluated by particle size and polydispersity index,morphology of ALA-LNs,and capacity of ALA loading.The dilution and pH stability of ALA-LNs suspensions were also studied.After three months storage,the mean size of ALA-LNs at 4 and 40 ℃ was increased by 2.68% and 3.62% compared with the original size,respectively.ALA-LNs stored at 40 ℃ had ellipsoid shape and the mean size was about 152 nm（SD=23.6）.The loading capacity of ALA at 40 ℃ was much higher than those stored at other two temperatures.The good dilution and pH stability were also demonstrated.The sample had good fluidity even at 4 ℃.
出处
《过程工程学报》
CAS
CSCD
北大核心
2010年第2期332-338,共7页
The Chinese Journal of Process Engineering
基金
Supported by International Scientific Cooperation Project of China (No.2008DFB50060)
Suzhou Innovation Funds of High-Tech Enterprise (No.SG0958)