摘要
Ce3＋-doped yttrium lanthanum oxide （Y0.9La0.1）2O3 transparent ceramics is fabricated with nanopowders and sintered in H2 atmosphere. The spectral properties of Ce：（Y0.9La0.1）2O3 transparent ceramics are investigated. There appear two characteristic absorption peaks of Ce3＋ ions at 230~nm and 400~nm, separately. It is found that Ce3＋ ions can efficiently produce emission at 384~nm from （Y0.9La0.1）2O3 transparent ceramic host, while the emission is completely quenched in Re2O3 （Re=Y, Lu, La） host materials.
Ce3＋-doped yttrium lanthanum oxide （Y0.9La0.1）2O3 transparent ceramics is fabricated with nanopowders and sintered in H2 atmosphere. The spectral properties of Ce：（Y0.9La0.1）2O3 transparent ceramics are investigated. There appear two characteristic absorption peaks of Ce3＋ ions at 230~nm and 400~nm, separately. It is found that Ce3＋ ions can efficiently produce emission at 384~nm from （Y0.9La0.1）2O3 transparent ceramic host, while the emission is completely quenched in Re2O3 （Re=Y, Lu, La） host materials.
基金
supported by the National Natural Science Foundation of China (Grant No. 60578041)
the Shanghai Leading Academic Disciplines (Grant No. S30107)