甲基丙烯酸2,2,2-三氟乙酯的原子转移自由基聚合

Atom transfer radical polymerization of 2,2,2-trifluoroethylmethacrylate
下载PDF
导出
摘要 以α-溴代丙酸乙酯(EPN-B)/CuCl/联二吡啶(bpy)作为引发/催化体系、环己酮为溶剂,对甲基丙烯酸2,2,2-三氟乙酯(TFEMA)进行原子转移自由基聚合(ATRP),研究了TFEMA的反应动力学,并考察了引发/催化体系、引发剂EPN-B用量、配位剂bpy用量及单体配比对聚合反应的影响。结果表明,采用EPN-B/CuCl/bpy引发/催化体系对TFEMA进行ATRP,可得到窄分子量分布的聚甲基丙烯酸2,2,2-三氟乙酯(PTFEMA),在实验范围内,聚合速率对单体浓度呈一级动力学关系,该反应过程具有活性聚合特征;随着引发剂EPN-B和配住剂bpy用量的增加,聚合速率加快,当EPN-B相对摩尔用量为0.5,1.0,2.0时,其相应的表观链增长速率常数分别为3.143×10^-4,3.478×10^-4,4.435×10^-4s^-1;增大[TFEMA]/[EPN-B](摩尔比),聚合速率明显降低,但无论[TFEMA]/[EPN-B]高与低,聚合物的分布指数均为1.15-1.23。 The atom transfer radical polymerization of 2,2,2-trifluoroethylmethacrylate (TFEMA) was conducted by using ethy1-2-bromopropionate (EPN-B)/cuprous chloride (CuCl)/bipyridine (bpy) as the initiating/catalytic system and cyclohexanone as solvent, polymerization kinetics of TFEMA was studied, and the effects of initiator/catalytic system, amount of initiator and complexant , mole ratio of monomer on polymerization rate were investigated. The results showed that the poly(2,2,2-trifluoroeth-ylmethacrylate) (PTFEMA) with narrow molecular weight distribution was obtained by using EPN-B/ CuCl/bpy as initiating/catalytic system. In the experiment range, the reation was first order in kinetics and behaved like living polymerization. The polymerization rate improved with increasing EPN-B and bpy, and the appatent chain constant was 3.143×10^-4,3.478×10^-4,4.435×10^-4s^-1 when the levels of EPN-B were 0.5, 1.0, 2.0 relative mole, respectively. The polymerization rate increased and polydispersion index (PDI) of PTFEMA decreased with increasing [TFEMA]/[EPN-B] (mole ratio) , but PDI kept at 1.15-1.23 no matter how the [TFEMA]/[EPN-B] (mole ratio)changed.
出处 《合成橡胶工业》 CAS CSCD 2009年第6期459-462,共4页 China Synthetic Rubber Industry
基金 国家自然科学基金资助项目(20774037)
关键词 甲基丙烯酸2 2 2-三氟乙酯 α-溴代丙酸乙酯 氯化亚铜 联二吡啶 原子转移自由基聚 反应动力学 2, 2, 2-trifluoroethylmethacrylate ethyl-2-bromopropionate cuprous chloride bipyri- dine atom transfer radical polymerization reaction kinetics
  • 引文网络
  • 相关文献

参考文献1

二级参考文献4

共引文献7

相关主题

;
使用帮助 返回顶部