摘要
Two crosslinkable poly（p-phenyleneethynylene）s（PPEs）： poly[2,5-di（2＇-ethyl-hexyloxy）-1,4-phenylenecthynylene] with end-capped vinyl（PPE1） and poly[2,5-di（allyloxy）-1,4-phenyleneethynylene-2,5-di（2＇-ethyl-hexyloxy）-1,4-phenyleneethynylene]（PPE2） were synthesized. Via the thermal addition reactions of vinyl end groups of PPE1 and allyloxy side groups of PPE2, crosslinked polymers C-PPE1 and C-PPE2 were obtained, respectively. The two polymers were characterized by wide-angle X-ray diffraction（WXRD）, ultraviolet-visible（UV-Vis） absorption, and photoluminescence（PL）. The results indicate that in the solid state, the polymer chains of PPE1 were packed with a low degree of crystallinity because of the sterically hindered（2＇-ethyl-hexyl）oxy branched side chains, but, because of the introduction of allyloxy side chains, the polymer chains of PPE2 were packed in an order fashion with a high degree of crystallinity. Because of the high crosslinking density in C-PPE2, the formation of aggregates and excimer was hampered by the formed crosslinking network more effectively in C-PPE2 film than in C-PPE1 film.
Two crosslinkable poly（p-phenyleneethynylene）s（PPEs）： poly[2,5-di（2＇-ethyl-hexyloxy）-1,4-phenylenecthynylene] with end-capped vinyl（PPE1） and poly[2,5-di（allyloxy）-1,4-phenyleneethynylene-2,5-di（2＇-ethyl-hexyloxy）-1,4-phenyleneethynylene]（PPE2） were synthesized. Via the thermal addition reactions of vinyl end groups of PPE1 and allyloxy side groups of PPE2, crosslinked polymers C-PPE1 and C-PPE2 were obtained, respectively. The two polymers were characterized by wide-angle X-ray diffraction（WXRD）, ultraviolet-visible（UV-Vis） absorption, and photoluminescence（PL）. The results indicate that in the solid state, the polymer chains of PPE1 were packed with a low degree of crystallinity because of the sterically hindered（2＇-ethyl-hexyl）oxy branched side chains, but, because of the introduction of allyloxy side chains, the polymer chains of PPE2 were packed in an order fashion with a high degree of crystallinity. Because of the high crosslinking density in C-PPE2, the formation of aggregates and excimer was hampered by the formed crosslinking network more effectively in C-PPE2 film than in C-PPE1 film.
基金
Supported by the National Natural Science Foundation of China(Nos.20771030 and 20671025)