High frequency ultrasonic nondestructive testing was conducted using a direct contact method for SUS306 stainless steel treated by high temperature and fracture tensile tests. Reflected ultrasonic echoes were analyzed. The relationships between the ultrasonic attenuation coefficient, strength of backscattering wave and the elongation at break of the samples were obtained. The damages were evaluated by using these results together with the analysis of microstructure and mechanics of the tested material.
High frequency ultrasonic nondestructive testing was conducted using a direct contact method for SUS306 stainless steel treated by high temperature and fracture tensile tests. Reflected ultrasonic echoes were analyzed. The relationships between the ultrasonic attenuation coefficient, strength of backscattering wave and the elongation at break of the samples were obtained. The damages were evaluated by using these results together with the analysis of microstructure and mechanics of the tested material.
基金
supported by the National Natural Science Foundation of China (Grant No.60472102)
the Innovative Program of Shanghai Municipal Education Commission (Grant No.07ZZ03)