The Ag-doping effects on Ti02 nanoparticles are investigated by means of x-ray diffraction （XRD） and Raman scattering spectroscopy. XRD and Raman results indicate that Ag-doping stabilizes the rutile phase in TiO2. We find an Ag-doping induced lattice expansion in both anatase and rutile phases. The Ag-doping has different influences on the lattice distortion for anatase and rutile phases, that is, the e/a-value for the anatase phase decreases with 0.5% Ag-doping and then increases with 1~ Ag-doping while that for the rutile phase shows a gradual increase with increasing Ag-doping. We have ascribed the different variations of lattice distortion due to Ag-doping to the change of interracial interaction between the anatase and rutile phases induced by different Ag concentrations.
The Ag-doping effects on Ti02 nanoparticles are investigated by means of x-ray diffraction （XRD） and Raman scattering spectroscopy. XRD and Raman results indicate that Ag-doping stabilizes the rutile phase in TiO2. We find an Ag-doping induced lattice expansion in both anatase and rutile phases. The Ag-doping has different influences on the lattice distortion for anatase and rutile phases, that is, the e/a-value for the anatase phase decreases with 0.5% Ag-doping and then increases with 1~ Ag-doping while that for the rutile phase shows a gradual increase with increasing Ag-doping. We have ascribed the different variations of lattice distortion due to Ag-doping to the change of interracial interaction between the anatase and rutile phases induced by different Ag concentrations.
基金
Supported by the National Natural Science Foundation of China under Grant Nos 10874088 and 10874087, the Key Project of the Ministry of Education of China under Grant No 107051, the Specialized Research Fund for the Doctoral Program of Higher Education of China under Grant No 200802840032, and State Key Laboratory of Electrical Insulation and Power Equipment, Xi＇an Jiaotong University （EIPE09202）.