Warm compaction and room temperature compaction were applied to prepare bonded Nd-Fe-B magnets. The results indicated that the density of magnet was determined by the compaction pressure and warm compaction temperature, whereas, the thermosetting temperature could hardly affect the density of magnet. The mechanical properties of magnets were the best when the thermosetting temperature was 200 ℃. The Br, Hob, and （BH）max of warm compaction magnet were higher than those of room compaction. When the warm compaction temperature and thermosetting temperature were invariable, the density of magnet increased with the increase of compaction pressure, which resulted in the increase of Br, Hcb, and （BH）max of magnet and the decrease of Hcj of magnet. When the warm compaction temperature and compaction pressure were invariable, the magnetic properties of magnets decreased with the increase of thermosetting temperature. The magnetic properties of warm compaction molding magnets were better than those of injection molding magnets.
Warm compaction and room temperature compaction were applied to prepare bonded Nd-Fe-B magnets. The results indicated that the density of magnet was determined by the compaction pressure and warm compaction temperature, whereas, the thermosetting temperature could hardly affect the density of magnet. The mechanical properties of magnets were the best when the thermosetting temperature was 200 ℃. The Br, Hob, and （BH）max of warm compaction magnet were higher than those of room compaction. When the warm compaction temperature and thermosetting temperature were invariable, the density of magnet increased with the increase of compaction pressure, which resulted in the increase of Br, Hcb, and （BH）max of magnet and the decrease of Hcj of magnet. When the warm compaction temperature and compaction pressure were invariable, the magnetic properties of magnets decreased with the increase of thermosetting temperature. The magnetic properties of warm compaction molding magnets were better than those of injection molding magnets.
基金
supported by the National Natural Science Foundation of China (Grant No.50074014)