摘要
Phase relationships in the Yb-Fe-Sb ternary system at 530 °C were investigated mainly by powder metallurgy and X-ray powder diffraction.Nine binary compounds（Yb6Fe23, Yb2Fe17, FeSb, FeSb2, YbSb2, YbSb, Yb11Sb10, Yb4Sb3, and αYb5Sb3） and one ternary compound（Fe4YbSb12） were confirmed in this system at 530 °C.The homogeneity range of FeSb phase extended from approximately 43at.%Sb to 45at.%Sb, the maximum solid solubility of Sb in Fe phase and Yb in FeSb phase was approximately 3at.%Sb and 1at.%Yb at 530 °C, respectively.Isothermal section of the phase diagram of the Yb-Fe-Sb ternary system at 530 °C consisted of thirteen single-phase regions, twenty-four two-phase regions, and twelve three-phase regions.
Phase relationships in the Yb-Fe-Sb ternary system at 530 °C were investigated mainly by powder metallurgy and X-ray powder diffraction.Nine binary compounds（Yb6Fe23, Yb2Fe17, FeSb, FeSb2, YbSb2, YbSb, Yb11Sb10, Yb4Sb3, and αYb5Sb3） and one ternary compound（Fe4YbSb12） were confirmed in this system at 530 °C.The homogeneity range of FeSb phase extended from approximately 43at.%Sb to 45at.%Sb, the maximum solid solubility of Sb in Fe phase and Yb in FeSb phase was approximately 3at.%Sb and 1at.%Yb at 530 °C, respectively.Isothermal section of the phase diagram of the Yb-Fe-Sb ternary system at 530 °C consisted of thirteen single-phase regions, twenty-four two-phase regions, and twelve three-phase regions.
基金
supported by the National Natural Science Foundation of China ( 50471108)