摘要
Green light-emitting Ba2SiO4：Eu^2＋ phosphors co-doped with La or Y were synthesized by conventional solid-state reaction technique in reductive atmosphere（a mixture of 5% H2 and 95% N2）.The results showed that the co-doping of La and Y could greatly enhance the fluorescence intensity of Ba2SiO4：Eu2＋ phosphors.The optimum doping concentration expressed by the x value in（Ba0.985-1.5xREx）2SiO4：0.03Eu^2＋（RE=La or Y） was determined to be of 0.05.The excitation and emission peaks of all as-synthesized phosphors were wide bands.The excitation bands ranged from 250 to 400 nm, which matched well with the wavelength of near ultraviolet white light-emitting diodes（LED） chip and could be used as a potential candidate for the fabrication of white LED.The emission bands from 450 to 550 nm were typical 5d-4f transition emission of Eu^2＋ and displayed un-symmetry profiles because of the two substitution sites of Ba^2＋ with Eu^2＋.
Green light-emitting Ba2SiO4：Eu^2＋ phosphors co-doped with La or Y were synthesized by conventional solid-state reaction technique in reductive atmosphere（a mixture of 5% H2 and 95% N2）.The results showed that the co-doping of La and Y could greatly enhance the fluorescence intensity of Ba2SiO4：Eu2＋ phosphors.The optimum doping concentration expressed by the x value in（Ba0.985-1.5xREx）2SiO4：0.03Eu^2＋（RE=La or Y） was determined to be of 0.05.The excitation and emission peaks of all as-synthesized phosphors were wide bands.The excitation bands ranged from 250 to 400 nm, which matched well with the wavelength of near ultraviolet white light-emitting diodes（LED） chip and could be used as a potential candidate for the fabrication of white LED.The emission bands from 450 to 550 nm were typical 5d-4f transition emission of Eu^2＋ and displayed un-symmetry profiles because of the two substitution sites of Ba^2＋ with Eu^2＋.
基金
Program for Changjiang Scholars and Innovative Research Team in University (IRT0730)
the Key Project of Department of Science and Technology of Jiangxi Province
Project of Education Department of Jiangxi