The effects of environmental media,both in atmosphere and in 3.5% NaCl aqueous solution, on the growth of short cracks in comparison with the long ones have been investigated under fatigue loading on the specimens of single-edge crack about 0.05—0.15 mm for A537CLI steel.The growth rate of short cracks is faster than those of long ones around the threshoht stress intensity.The threshold stress intensity for short crack growth decreases with de- creasing crack length.The acceleration effect of the salt water,as compared with atmosphere environment,on the growth of short cracks under fatigue is much greater than that on the growth of long cracks.
The effects of environmental media,both in atmosphere and in 3.5% NaCl aqueous solution, on the growth of short cracks in comparison with the long ones have been investigated under fatigue loading on the specimens of single-edge crack about 0.05—0.15 mm for A537CLI steel.The growth rate of short cracks is faster than those of long ones around the threshoht stress intensity.The threshold stress intensity for short crack growth decreases with de- creasing crack length.The acceleration effect of the salt water,as compared with atmosphere environment,on the growth of short cracks under fatigue is much greater than that on the growth of long cracks.