The interaction of hydrogen with interface between the precipitates and the martensitie matrix in 18Ni maraging steel has been studied by means of thermal evolution hydrogen technique us- ing gas chromatograph as hydrogen detector.An evolution rate peak has been observed at 451 K.The height of the peak relates to the amount and distribution of the precipitates.The activation energy for hydrogen escaping from the trap sites is 23.2 kJ/mol.
The interaction of hydrogen with interface between the precipitates and the martensitie matrix in 18Ni maraging steel has been studied by means of thermal evolution hydrogen technique us- ing gas chromatograph as hydrogen detector.An evolution rate peak has been observed at 451 K.The height of the peak relates to the amount and distribution of the precipitates.The activation energy for hydrogen escaping from the trap sites is 23.2 kJ/mol.