Polysulfonamide/zinc oxide(PSA/ZnO) nanocomposite films with w(ZnO)=0.5% were prepared by in-situ polymerization based on 4,4′-diaminodiphenylsulfone and terephthaloyl chloride in the common solvent N,N-Dimethylacetamide(DMAc). Atomic force microscopy (AFM) was employed to observe the microstructure of the composite film. The thermal property was investigated by TGA and mechanical property was characterized by DXLL-1000 electromechanical material testing machine. The results showed that the breaking strength of the film containing 0.5% ZnO was great enhanced. The average size of ZnO particles was below 100 nm. The introduction of ZnO as nano filler in PSA react as UV shield effect and make the composite mechanical property improved.
Polysulfonamide/zinc oxide(PSA/ZnO) nanocomposite films with w(ZnO)=0.5% were prepared by in-situ polymerization based on 4,4′-diaminodiphenylsulfone and terephthaloyl chloride in the common solvent N,N-Dimethylacetamide(DMAc). Atomic force microscopy (AFM) was employed to observe the microstructure of the composite film. The thermal property was investigated by TGA and mechanical property was characterized by DXLL-1000 electromechanical material testing machine. The results showed that the breaking strength of the film containing 0.5% ZnO was great enhanced. The average size of ZnO particles was below 100 nm. The introduction of ZnO as nano filler in PSA react as UV shield effect and make the composite mechanical property improved.
基金
Education Commission of Shanghai (No04AB19)
Science and Technology Commission of Shanghai Municipal Government(Nano Founds No 0452NM051)