The aim of this work is to attempt the application of A357 Al-Si-Mg cast alloy in the thixoextrusion process,evaluating the different forming parameters effect.Thixoextrusion offers several advantages compared with traditional hot-extrusion such as lower pressure,minor friction forces,higher material fluidity and longer tool life.This type of semi-solid process requires high solid fraction(0.7<fs<1) materials because of its low solidification rate.Aluminium alloy A357 is a commercial cast alloy characterized by high strength,ductility and corrosion resistance.It is commonly used for cast production of automotive components and it is also suitable for semi-solid process,due to its wide range of solidification.A357 aluminium alloy was used as a feedstock for thixoextrusion in order to investigate thixoformability at high solid fraction.A357 alloy with high solid fraction(>0.85) is less sensitive to temperature drops and allows more stable material flow at higher speeds.To know the forming parameters that improve the mechanical properties of thixoextruded parts,some extrusion tests were carried out.The results were used as the main criteria for assessing the thixoforming viability of the A357 alloy.
The aim of this work is to attempt the application of A357 Al-Si-Mg cast alloy in the thixoextrusion process,evaluating the different forming parameters effect.Thixoextrusion offers several advantages compared with traditional hot-extrusion such as lower pressure,minor friction forces,higher material fluidity and longer tool life.This type of semi-solid process requires high solid fraction(0.7<fs<1) materials because of its low solidification rate.Aluminium alloy A357 is a commercial cast alloy characterized by high strength,ductility and corrosion resistance.It is commonly used for cast production of automotive components and it is also suitable for semi-solid process,due to its wide range of solidification.A357 aluminium alloy was used as a feedstock for thixoextrusion in order to investigate thixoformability at high solid fraction.A357 alloy with high solid fraction(>0.85) is less sensitive to temperature drops and allows more stable material flow at higher speeds.To know the forming parameters that improve the mechanical properties of thixoextruded parts,some extrusion tests were carried out.The results were used as the main criteria for assessing the thixoforming viability of the A357 alloy.
出处
《中国有色金属学会会刊：英文版》
CSCD
2010年第S3期1005-1009,共5页
Transactions of Nonferrous Metals Society of China
基金
the University of Liège for the experimental support
the Walloon Region (First Europe project)
the COST 541 for their financial support