采用二次水热法,在Pt/Al2O3球形催化剂颗粒上合成了致密的NaA分子筛膜.分别以X射线衍射(XRD)和扫描电子显微镜(SEM)对制备的分子筛膜催化剂结构及形貌进行表征,结果显示经二次合成的Pt/Al2O3球形催化剂颗粒上均匀地覆盖一层致密、均一的NaA分子筛膜,膜的厚度约为20"m.将合成的NaA分子筛膜催化剂用于CO和C2H4混合气氧化反应,考察了催化剂表面分子筛膜对反应物分子的选择性,在最优条件下,CO对C2H4的氧化反应选择性始终维持在96%.这种复合膜催化剂可用于选择性除去C2H4原料气中的CO.
Defect-free zeolite NaA membranes were coated onto the surface of spherical Pt/Al2O3 particles using a two-step hydrothermal method. The structure and morphology of the synthesized composite catalysts were characterized using XRD and SEM techniques, respectively. The results indicated a layer of compact and uniform NaA molecular sieve membrane with a thickness of about 20 μm was coated on the spherical Pt/Al2O3 particles after the two-step hydrothermal synthesis. The prepared NaA membrane coated catalysts were used in the oxidation of a mixture of CO and C2H4 to study the reactant selectivity over the coated zeolite NaA membranes. Under the optimized conditions, the oxidation selectivity for CO over C2H4 on the composite catalyst was as high as 96%. The feasible application of this composite membrane coated catalyst to the selective removal of CO in the presence of C2H4 was anticipated.
出处
《物理化学学报》
SCIE
CAS
CSCD
北大核心
2008年第10期1875-1878,共4页
Acta Physico-Chimica Sinica
基金
国家自然科学基金(20471052)资助项目