摘要
应用小角X射线散射(SAXS)技术研究1420合金时效-回归-再时效析出δ′相的行为.结果表明,再时效处理5 h后析出的δ′相与基体间存在明显的过渡界面层,再时效48 h后过渡界面层消失,时效80 h和再时效80 h析出δ′相的回转半径分别为9.32 nm和8.27 nm.再时效过程中δ′相粒子的长大速度比回归前慢,随着再时效时间的增加,粒子非均匀长大.
Small-angle X-ray scattering （SAXS） was used to study the precipitation behavior of the δ＇ phase in 1420 alloy treated by aging-retrogression-reaging. The results show that the transition interfacial layer exists between the δ＇ phase and the matrix after reaging for 5 h, but the transition interracial layer disappears after reaging for 48 h. The gyration radius of the δ＇ phase particles, RG was 9.32 nm for aging 80 h and 8.27 nm for reaging 80 h, respectively. This suggests that the δ＇ phase particles coarsen is much slower during reaging treatment compared with that of aging treatment. With the reaging time increase, the δ＇ phase grain size is not the same.