摘要
以可膨化石墨为原料,高温处理得到膨化石墨,再经过超声处理,得到纳米薄片石墨。将得到的纳米薄片石墨与甲基丙烯酸甲酯单体在超声作用下预聚,灌模,得到块状的聚甲基丙烯酸甲酯(PMMA)/石墨复合材料。用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、选区电子衍射SAD、红外、热重等分析仪器表征了纳米石墨薄片及PMMA/石墨复合材料。测试了复合材料的力学、电学性能,发现在室温下该复合材料的渗滤阀值为1.3%(wt),且保证石墨含量在1.4%(wt)时,即可保证复合材料具有良好的电学和力学性能。
Expandable graphite was used to prepare graphite nanosheets by heating treatment and sonication. The PMMA/graphite composite was prepared by in-suit bulk polymerization using the expanded graphite and MMA. SEM,TEM,SAD,FTIR and TG were used to characterize PMMA/graphite composite. The impact test and electrical conductivity were measured. It was found that the percolation threshold of the composite was about 1.3% （ wt ） and the composite will have good conductive properties and good impact properties when the content of graphite is less than 1.4% （wt）.
出处
《化学研究与应用》
CAS
CSCD
北大核心
2008年第7期848-853,共6页
Chemical Research and Application
基金
国家自然科学重点项目(20736004)
国家自然科学基金(20476065)项目
教育部留学回国基金项目
中科院过程工程研究所多相反应复杂系统国家重点实验室(2006-5)项目
中科院煤炭化学研究所煤转化国家重点实验室(2006-902)项目
有机合成江苏省重点实验室项目
苏州大学基础课化学实验教学中心项目
南京医科大学研发基金项目(NY0586)