摘要
研究了无取向硅钢Ｗ２３Ｇ，Ｗ１０，Ｗ１４和取向硅钢Ｑ８Ｇ４种材料在不同形变量下的磁声发射（ＭＡＥ）和巴克豪森噪音（ＢＮ），结果表明ＭＡＥ随形变量增大而减少，ＢＮ随形变量的增大而增大．测量了形变量为１０．４％的Ｗ１８和Ｗ２３Ｇ在１００，２００，３００，…，７００°Ｃ各退火１ｈ的ＭＡＥ与ＢＮ值．其中ＭＡＥ值随退火温度的升高逐渐增大，ＢＮ值在高于５００°Ｃ退火时明显下降．并对上述实验结果进行了详细讨论．
This paper investigated magnetic acoustic emition(MAE) and Barkhausen noise(BN) of non oriented Fe Si alloy W 23 G,W 10 ,W 14 and oriented Fe Si alloy Q 8G under different deformation. The results show that MAE decreases and BN increases with the deformation increasing. MAE and BN of W 18 and W 23 G deformed 10.4% were measured after the samples were annealed at 100,200,300,…,700 °C respectively for one hour. MAE increases gradully as annealing temperature go up, and BN decreases obviously when it is annealed above 500 °C. The experiment results were discussed.