以BaTiO3、CYD128型环氧树脂、丁腈橡胶和4,4-二氨基二苯基砜为原料,采用共混法制备了具有高介电常数和低介电损耗性能的BaTiO3/环氧复合材料。实验结果表明,环氧树脂中添加BaTiO3后,介电常数从4提高到25,介电损耗从0.4%提高到0.7%。丁腈橡胶的加入使复合材料的介电常数进一步提高到41,介电损耗提高到1.7%,体积电阻率降低到1×1011Ω,击穿强度保持在8kV/mm。Lichtenecker模型计算表明,环氧树脂中BaTiO3的有效介电常数为343,丁腈橡胶为138。
A kind of BaTiO3/epoxy composite material with high dielectric constant and low dielectric dissipation was prepared by mixing method. The composite was prepared with BaTiO3, epoxy resin CYD128, 4,4-diaminodiphenyl sulphone and nitrile-butadiene rubber. Experimental results indicated that BaTiO3 could increase dielectric constant of the epoxy resin from 4 to 25, and dielectric dissipation factor from 0.4% to 0.7%. Nitrile-butadiene rubber increased the dielectric constant of the BaTiO3/epoxy composite from 25 to 41, and the dielectric dissipation factor from 0.0012 to 0.0017, while the volume resistivity was decreased from 6 ×10^11Ω· m to 1×10^11Ω·m, the breakdown voltage was kept in same level of 8kV/mm. Derived from Lichtenecker＇ s Rule, effective dielectric constant of the BaTiO3 was 343 and the nitrile-butadiene rubber was 138 in the epoxy resin matrix. A new method of preparation embedded capacitor with low cost industrially was explored.
出处
《材料科学与工程学报》
CAS
CSCD
北大核心
2007年第6期914-916,共3页
Journal of Materials Science and Engineering
关键词
介电常数
内埋式电容器
丁腈橡胶
dielectric constant
embedded capacitor
nitrile-butadiene rubber