Mg(OH)2 nano-particles with fiber-like morphology were prepared by chemical precipitation process,with the bittern from Qinghai Salt Lakes used as Mg2+ raw material and ammonia water as precipitator. The influence of aging procedure on the Mg(OH)2 crystal was investigated by TEM and crystalline size calculation. The Mg(OH)2 nano-particles were characterized by XRD,SEM,TEM and TG-DTA methods. The results indicate that the Mg(OH)2 nano-particles with perfect crystal are obtained after aging procedure above 50 ℃,and the grain size increases with increasing aging temperature and prolonging aging time. Mg(OH)2 particles with fiber-like morphology,20-60 nm in diameter and 300-500 nm in length are observed,Mg(OH)2 will decompose into MgO at temperature range 347-623 ℃.
Mg（OH）2 nano-particles with fiber-like morphology were prepared by chemical precipitation process, with the bittern from Qinghai Salt Lakes used as Mg^2＋ raw material and ammonia water as precipitator. The influence of aging procedure on the Mg（OH）2 crystal was investigated by TEM and crystalline size calculation. The Mg（OH）2 nano-particles were characterized by XRD, SEM, TEM and TG-DTA methods. The results indicate that the Mg（OH）2 nano-particles with perfect crystal are obtained after aging procedure above 50 ℃, and the grain size increases with increasing aging temperature and prolonging aging time. Mg（OH）2 particles with fiber-like morphology, 20-60 nm in diameter and 300-500 nm in length are observed, Mg（OH）2 will decompose into MgO at temperature range 347-623℃.
出处
《中国有色金属学会会刊：英文版》
CSCD
2007年第A02期671-674,共4页
Transactions of Nonferrous Metals Society of China
基金
Project supported by Promoting Program of National Engineering Laboratory for Vacuum Metallurgy
关键词
纳米颗粒
纳米材料
制备方法
氢氧化镁
盐卤
magnesium hydroxide
nano-particles
chemical precipitation
bittern