通过正交试验法研究了成分变化对TiC-WC-Cr3C2-16wt%(Co+Ni)-Mo金属陶瓷耐腐蚀性能的影响。结果表明,本试验中A2B4C2为TiC基金属陶瓷最佳耐腐蚀配方组合;在TiC基金属陶瓷中,Mo含量和Co/Ni含量比对合金的抗腐蚀性能影响最大。
The effect of composition on corrosion resistance of TiC-based （TiC-WC-Cr3C2-Co-Ni-Mo） cermet was investigated through orthogonal experiments. The optimal composition was determined. The content of Mo and the Co/Ni ratio were the main factors affecting the corrosion resistance of cermet.