摘要
A highly ordered m-phenylenediimino-bridged ladder polyhydrosiloxane （abbr. OLPHS） with Mn = 1.24 × 10^4 was synthesized stoichiometric hydrolysis and dehydrochlorination condensation reaction between Si-Cl and Si-OH bonds. The complete ladder structure of OLPHS has been confirmed by the following three data. Two characteristic Bragg＇s peaks representing the ladder width （w = 0.94 nm） and ladder thickness （t = 0.42 nm） were observed in XRD analysis, which are consistent with those calculated by molecular simulation. The very sharp absorption with a small half-peak width （w1/2 = 0.5 ppm） for [（-HN）HSiO2/2]n moiety of OLPHS in ^29Si NMR spectrum indicated presence of the complete ladder structure. As collateral evidence, a higher glass transition temperature （Tg = 105 ℃） is also recorded in the DSC measurement, implying the high stiffness of ladder chain of OLPHS.
A highly ordered m-phenylenediimino-bridged ladder polyhydrosiloxane （abbr. OLPHS） with Mn = 1.24 × 10^4 was synthesized stoichiometric hydrolysis and dehydrochlorination condensation reaction between Si-Cl and Si-OH bonds. The complete ladder structure of OLPHS has been confirmed by the following three data. Two characteristic Bragg＇s peaks representing the ladder width （w = 0.94 nm） and ladder thickness （t = 0.42 nm） were observed in XRD analysis, which are consistent with those calculated by molecular simulation. The very sharp absorption with a small half-peak width （w1/2 = 0.5 ppm） for [（-HN）HSiO2/2]n moiety of OLPHS in ^29Si NMR spectrum indicated presence of the complete ladder structure. As collateral evidence, a higher glass transition temperature （Tg = 105 ℃） is also recorded in the DSC measurement, implying the high stiffness of ladder chain of OLPHS.