摘要
以甲基丙烯酸羟乙酯为原料,过硫酸铵/偏重亚硫酸钠为引发体系,二甲基丙烯酸三乙二醇酯为交联剂,采用溶液聚合法制备了聚甲基丙烯酸羟乙酯水凝胶(PHEMA)人工晶状体材料。系统考察了聚合反应时间、温度及引发剂和交联剂的用量等对该水凝胶材料机械强度、平衡水含量(EWC)的影响,并对PHEMA水凝胶的结构和光学性能进行了表征。实验结果表明,PHEMA水凝胶的最佳合成条件为:引发剂0.5wt%,交联剂1.0wt%,反应温度40℃,反应时间36h。在此条件下制备的PHEMA水凝胶的拉伸强度达到0.57MPa,邵氏A硬度为23.0,平衡含水量超过40%,透光率≥97%。
Poly （hydroxyethyl methacrylate） （PHEMA） hydrogel for intraocular lens （IOL） materials was synthesized by solution polymerization using 2-hydroxyethyl methacrylate （HEMA） as raw material, ammonium persulfate and sodium pyrosulfite （KPS/SMBS） as catalyst, and trietyleneglycole dimethacrylate （TEGDMA） as cross-linking additive. Effects of reaction time, temperature, dosage of catalyst and cross-linking additive on mechanical strength and the equilibrium water content （EWC） of the PHEMA hydrogel were systematically investigated and their structure and optical property were also characterized. The experimental results showed that the optimum conditions for preparing PHEMA hydrogel are： catalyst 0. 5wt %, cross-linking additive 1.0wt %, reaction temperature 40℃, reaction time 36 h. Under the optimum conditions, the tensile strength of PHEMA hydrogel prepared is as high as 0.57MPa, hardness of Shore A is 23.0, EWC is over 40%, and light transmittance is over 97%.
出处
《生物医学工程学杂志》
EI
CAS
CSCD
北大核心
2007年第3期595-598,共4页
Journal of Biomedical Engineering
基金
华南理工大学"学生研究计划"项目
关键词
聚甲基丙烯酸2-羟乙酯
水凝胶
人工晶状体材料
合成
性能
Poly （hydroxyethyl methacrylate） （PHEMA） Hydrogel Intraocular lens （IOL） materials Synthesis Property