Silica aerogels were prepared at ambient drying by using ethanol/trimethylchlorosilane （TMCS）/heptane solution as pore water exchange and surface modification of the wet gel before drying. The obtained silica aerogels exhibit a sponge-like structure with uniform pore size distribution. The effects of heat-treatment on the hydrophobicity, specific surface area and other properties were investigated. The results indicated that the hydrophobicity of silica aerogels could be maintained up to 350℃. With increasing heating temperature, hydrophobicity decreased, and became completely hydrophilic after heat-treatment at 500℃. Brunaueremmitt-teller （BET） surface area results indicated that the specific surface area of silica aerogels increased with increasing heating temperature in the range of 150-500℃. The effects of heat-treatment on the morphology and chemical bonding state of silica aerogels were investigated by scanning electron microscopy （SEM）, differential temperature analysis （DTA） and Fourier-transform infrared spectroscopy （FT-IR）.
Silica aerogels were prepared at ambient drying by using ethanol/trimethylchlorosilane （TMCS）/heptane solution as pore water exchange and surface modification of the wet gel before drying. The obtained silica aerogels exhibit a sponge-like structure with uniform pore size distribution. The effects of heat-treatment on the hydrophobicity, specific surface area and other properties were investigated. The results indicated that the hydrophobicity of silica aerogels could be maintained up to 350℃. With increasing heating temperature, hydrophobicity decreased, and became completely hydrophilic after heat-treatment at 500℃. Brunaueremmitt-teller （BET） surface area results indicated that the specific surface area of silica aerogels increased with increasing heating temperature in the range of 150-500℃. The effects of heat-treatment on the morphology and chemical bonding state of silica aerogels were investigated by scanning electron microscopy （SEM）, differential temperature analysis （DTA） and Fourier-transform infrared spectroscopy （FT-IR）.