Electroplating zinc coating as transition layer of electroless nickel plating on AM60 magnesium alloys was investigated. The zinc film can be deposited in a pyrophosphate bath at 50-60℃under current density of 0.5-1.5 A/dm2. A new fore treatment technology was applied by acid cleaning with a solution containing molybdate and phosphorous acid, by alkaline cleaning in a bath containing molybdate and sodium hydroxide. The subsequent electroless plating was carried out in nickel sulfate bath. The SEM observation shows that the deposition is uniform and compact. The polarization curve measurements show that the corrosion potential of the zinc plating in 3.5% NaCl is about -1.3 V(vs SCE) which is noble than that of magnesium substrate. The zinc electroplating can be applied as the pretreatment process for electroless nickel plating on magnesium alloys.
Electroplating zinc coating as transition layer of electroless nickel plating on AM60 magnesium alloys was investigated. The zinc film can be deposited in a pyrophosphate bath at 50-60 ℃ under current density of 0.5-1.5 A/dm^2. A new fore treatment technology was applied by acid cleaning with a solution containing molybdate and phosphorous acid, by alkaline cleaning in a bath containing molybdate and sodium hydroxide. The subsequent electroless plating was carried out in nickel sulfate bath. The SEM observation shows that the deposition is uniform and compact. The polarization curve measurements show that the corrosion potential of the zinc plating in 3.5% NaCl is about -1.3 V（vs SCE） which is noble than that of magnesium substrate. The zinc eleetroplating can be applied as the pretreatment process for electroless nickel plating on magnesium alloys.
出处
《中国有色金属学会会刊：英文版》
CSCD
2006年第A03期1798-1801,共4页
Transactions of Nonferrous Metals Society of China
基金
Project (202113191) supported by the Science Fund of Education Office of Liaoning Province, China
Project supported by the Director Fund of Experimental Centre of Shenyang Normal University, China
关键词
电镀工艺
锌
镍
镁合金
金属处理
magnesium alloy
AM60
electroplating zinc
electroless nickel plating
corrosion resistance