摘要
速生杉木的材性逊于非速生杉木。气干密度０．３４５ｇ·ｃｍ－３，体积干缩系数０．４４４％，顺纹抗压强度２８．０ＭＰａ，静力弯曲强度５７．０ＭＰａ，静力弯曲弹性模量８．５ＧＰａ．
The wood properties of fast-growing Chinese fir wer e worse than the ones of common
Chiness fir.For the former, air-drying density was 0.345g、cm,volumetric shrinkage coefficient
was 0.444%compressive strength parallel to the grainrupture strength in static bending and elastic
modulus in static bending was 28.0 MPa,57.0 MPa and 8.5 GPa respectively.